S6/S6-TW Oil Resistant Polyolefin Elastomer Heat Shrink Tubing
Keywords:
S6/S6-TW Oil Resistant Polyolefin Elastomer Heat Shrink Tubing
Category:
Heat shrink products in military and aerospace fields
Hot-line:
Details
Introduction | |||
A soft radiation cross-linked polyolefin elastomer heat-shrinkable tube is used for the connection, insulation and protection of various wires and cables in military equipment that need to be resistant to temperature and oil. Insulation protection or coating, electronic |
Features | ||
Operating temperature: -75~150 ℃ | ||
Minimum full shrinkage temperature: 150 ℃ | ||
Shrink ratio: 2:1 | ||
GJB 7274-2011 compliant | ||
Excellent resistance to diesel, lubricating oil and hydraulic oil | ||
soft, flame retardant |
Technical data | ||||
Property | Test Method | Value | ||
Density | GJB 7274-2011 | ≤1.50g/cm3 | ||
Longitudinal change rate | GJB 7274-2011 | -10%~10% | ||
Restricted shrinkage(200℃/30分钟) | GJB 7274-2011 | No cracks on the surface | ||
Water absorption (23℃/24h) | GJB 7274-2011 | ≤2.0% | ||
Tensile Strength | GJB 7274-2011 | ≥11.7MPa | ||
Breakdown elongation | GJB 7274-2011 | ≥250% | ||
Heat shock (200℃/4h) | GJB 7274-2011 | No cracks, no flow, no dripping on the surface | ||
Aging(150℃/168h) Tensile Strength Breakdown elongation |
GJB 7274-2011 | ≥10.4MPa ≥200% |
||
Dielectric strength | GJB 7274-2011 | ≥11.9kV/mm | ||
Insulation withstand voltage(AC2500V·1min.) | GJB 7274-2011 | Not broken down | ||
Volume resistivity | GJB 7274-2011 | ≥1.0×109Ω·cm | ||
Liquid resistance(23℃/24h) Tensile Strength Breakdown elongation Dielectric strength |
GJB 7274-2011 | ≥ 10.4MPa ≥200% ≥7.9kV/mm |
||
flame retardancy | GJB 7274-2011 | The continuous burning time does not exceed 60S after leaving the fire | ||
Copper corrosion(135℃/16h) | GJB 7274-2011 | No dents or blackening of the copper surface | ||
low temperature flexibility(-55℃/4h) | GJB 7274-2011 | No cracks on the surface | ||
High and low temperature impact(-55℃/120℃) | GJB 7274-2011 | Tensile Strength≥10.4MPa 断裂伸长率≥200% |
||
salt spray | GJB 150.11 | 拉伸强度≥10.4MPa 断裂伸长率≥200% |
||
damp heat | GJB 150.9 | 拉伸强度≥10.4MPa 断裂伸长率≥200% |
||
mold | GJB 150.10 | 长霉程度不劣于1级 |
Dimension | |||||
规格 | As Supplied(mm) | After shrink (mm) | Wire mass(Max.) | Standard length | |
Inner Diameter(Min.) | Inner Diameter (Max.) | Wall thickness | g/m | m | |
常规壁厚 S6 | |||||
1.6/0.85 | 1.6 | 0.85 | 0.40±0.08 | 3.1 | 200 |
2.4/1.2 | 2.4 | 1.2 | 0.51±0.08 | 5.9 | 200 |
3.2/1.6 | 3.2 | 1.6 | 0.76±0.15 | 9.6 | 200 |
4.8/2.4 | 4.8 | 2.4 | 0.84±0.15 | 14.7 | 200 |
6.4/3.2 | 6.4 | 3.2 | 0.89±0.15 | 19.3 | 200 |
9.5/4.8 | 9.5 | 4.8 | 1.02±0.20 | 31.5 | 122 |
12.7/6.4 | 12.7 | 6.4 | 1.22±0.20 | 42.5 | 122 |
15.9/7.9 | 15.9 | 7.9 | 1.32±0.28 | 57.5 | 61 |
19.1/9.5 | 19.1 | 9.5 | 1.45±0.28 | 80.1 | 61 |
22.2/11.1 | 22.2 | 11.1 | 1.55±0.28 | 98.5 | 61 |
25.4/12.7 | 25.4 | 12.7 | 1.78±0.28 | 120.0 | 61 |
31.8/15.9 | 31.8 | 15.9 | 2.20±0.41 | 172.5 | 30.4 |
38.1/19.1 | 38.1 | 19.1 | 2.41±0.41 | 243.0 | 30.4 |
50.8/25.4 | 50.8 | 25.4 | 2.79±0.41 | 342.0 | 30.4 |
薄壁 S6-TW | |||||
1.6/0.85 | 1.6 | 0.85 | 0.40±0.08 | 3.1 | 200 |
2.4/1.2 | 2.4 | 1.2 | 0.51±0.08 | 5.9 | 200 |
3.2/1.6 | 3.2 | 1.6 | 0.51±0.08 | 7.0 | 200 |
4.8/2.4 | 4.8 | 2.4 | 0.51±0.08 | 9.6 | 200 |
6.4/3.2 | 6.4 | 3.2 | 0.64±0.08 | 15.6 | 200 |
9.5/4.8 | 9.5 | 4.8 | 0.64±0.08 | 22.2 | 122 |
12.7/6.4 | 12.7 | 6.4 | 0.64±0.08 | 27.0 | 122 |
15.9/7.9 | 15.9 | 7.9 | 0.76±0.15 | 37.6 | 61 |
19.1/9.5 | 19.1 | 9.5 | 0.76±0.15 | 47.2 | 61 |
22.2/11.1 | 22.2 | 11.1 | 0.89±0.15 | 60.2 | 61 |
25.4/12.7 | 25.4 | 12.7 | 0.89±0.15 | 67.6 | 61 |
31.8/15.9 | 31.8 | 15.9 | 1.02±0.20 | 90.4 | 30.4 |
38.1/19.1 | 38.1 | 19.1 | 1.02±0.20 | 115.4 | 30.4 |
50.8/25.4 | 50.8 | 25.4 | 1.14±0.20 | 157.9 | 30.4 |