S6-T Polyurethane Elastomer Heat Shrink Tubing
Keywords:
S6-T Polyurethane Elastomer Heat Shrink Tubing
Category:
Heat shrink products in military and aerospace fields
Hot-line:
Details
Introduction | |||
A soft radiation cross-linked polyurethane elastomer heat-shrinkable tube is used for the connection, insulation and protection of various wires and cables in military equipment that require wear-resistant and solvent-resistant environments, end treatment or insulation protection or coating of wiring, electronic Component wrapping, etc. |
Features | ||
Operating temperature: -55~125 ℃ | ||
Minimum full shrinkage temperature: 150 ℃ | ||
Shrink ratio: 2:1 | ||
GJB 7274-2011 compliant | ||
Excellent wear resistance, lubricating oil resistance, hydraulic oil performance | ||
soft, flame retardant |
Technical data | ||||
Property | Test Method | Value | ||
Density | GJB 7274-2011 | ≤1.50g/cm3 | ||
Longitudinal change rate | GJB 7274-2011 | -10%~10% | ||
Restricted shrinkage(200℃/30m) | GJB 7274-2011 | No cracks on the surface | ||
Water absorption (23℃/24小时) | GJB 7274-2011 | ≤2.0% | ||
Tensile Strength | GJB 7274-2011 | ≥11.7MPa | ||
Breakdown elongation | GJB 7274-2011 | ≥250% | ||
Heat shock(200℃/4h) | GJB 7274-2011 | No cracks, no flow, no dripping on the surface | ||
h(150℃/168h) Tensile Strength Breakdown elongation |
GJB 7281-2011 | ≥10.4MPa ≥200% |
||
Dielectric strength | GJB 7274-2011 | ≥11.9kV/mm | ||
Insulation withstand voltage(AC2500V·1min.) | GJB 7274-2011 | Not broken down | ||
Volume resistivity | GJB 7274-2011 | ≥1.0×109Ω·cm | ||
Liquid resistance(23℃/24h) Tensile Strength Breakdown elongation |
GJB 7274-2011 | ≥70% of the initial value ≥100% |
||
flame retardancy | GJB 7274-2011 | The continuous burning time does not exceed 60S after leaving the fire | ||
Copper corrosion(135℃/16h) | GJB 7274-2011 | No dents or blackening of the copper surface | ||
low temperature flexibility(-55℃/4h) | GJB 7274-2011 | No cracks on the surface | ||
High and low temperature impact(-55℃/120℃) | GJB 7274-2011 | Tensile Strength≥70% of the initial value Breakdown elongation≥200% |
||
salt spray | GJB 150.11 | Tensile Strength≥70% of the initial value Breakdown elongation≥200% |
||
damp heat | GJB 150.9 | Tensile Strength≥70% of the initial value Breakdown elongation≥200% |
||
mold | GJB 150.10 | The degree of mold growth is not worse than grade 1 |
Dimension | |||||
Size | As Supplied(mm) | After shrink (mm) | Wire mass(Max.) | Standard length | |
S6-T | Inner Diameter(Min.) | Inner Diameter (Max.) | Wall thickness | g/m | m |
Regular wall thickness S6-T | |||||
1.6/0.85 | 1.6 | 0.85 | 0.40±0.08 | 3.1 | 200 |
2.4/1.2 | 2.4 | 1.2 | 0.51±0.08 | 5.9 | 200 |
3.2/1.6 | 3.2 | 1.6 | 0.76±0.15 | 9.6 | 200 |
4.8/2.4 | 4.8 | 2.4 | 0.84±0.15 | 14.7 | 200 |
6.4/3.2 | 6.4 | 3.2 | 0.89±0.15 | 19.3 | 200 |
9.5/4.8 | 9.5 | 4.8 | 1.02±0.20 | 31.5 | 122 |
12.7/6.4 | 12.7 | 6.4 | 1.22±0.20 | 42.5 | 122 |
15.9/7.9 | 15.9 | 7.9 | 1.32±0.28 | 57.5 | 61 |
19.1/9.5 | 19.1 | 9.5 | 1.45±0.28 | 80.1 | 61 |
22.2/11.1 | 22.2 | 11.1 | 1.55±0.28 | 98.5 | 61 |
25.4/12.7 | 25.4 | 12.7 | 1.78±0.28 | 120.0 | 61 |
31.8/15.9 | 31.8 | 15.9 | 2.20±0.41 | 172.5 | 30.4 |
38.1/19.1 | 38.1 | 19.1 | 2.41±0.41 | 243.0 | 30.4 |
50.8/25.4 | 50.8 | 25.4 | 2.79±0.41 | 342.0 | 30.4 |
thin wall S6-TTW | |||||
1.6/0.85 | 1.6 | 0.85 | 0.40±0.08 | 3.1 | 200 |
2.4/1.2 | 2.4 | 1.2 | 0.51±0.08 | 5.9 | 200 |
3.2/1.6 | 3.2 | 1.6 | 0.51±0.08 | 7.0 | 200 |
4.8/2.4 | 4.8 | 2.4 | 0.51±0.08 | 9.6 | 200 |
6.4/3.2 | 6.4 | 3.2 | 0.64±0.08 | 15.6 | 200 |
9.5/4.8 | 9.5 | 4.8 | 0.64±0.08 | 22.2 | 122 |
12.7/6.4 | 12.7 | 6.4 | 0.64±0.08 | 27.0 | 122 |
15.9/7.9 | 15.9 | 7.9 | 0.76±0.15 | 37.6 | 61 |
19.1/9.5 | 19.1 | 9.5 | 0.76±0.15 | 47.2 | 61 |
22.2/11.1 | 22.2 | 11.1 | 0.89±0.15 | 60.2 | 61 |
25.4/12.7 | 25.4 | 12.7 | 0.89±0.15 | 67.6 | 61 |
31.8/15.9 | 31.8 | 15.9 | 1.02±0.20 | 90.4 | 30.4 |
38.1/19.1 | 38.1 | 19.1 | 1.02±0.20 | 115.4 | 30.4 |
50.8/25.4 | 50.8 | 25.4 | 1.14±0.20 | 157.9 | 30.4 |
Ordering instructions: please order by "model-specification-color", such as S6-T-9.5/4.8-0 | |||
Color: Black (-0) should be used |