S10 Soft Viton Heat Shrinkable Tube
Keywords:
Category:
Heat shrink products in military and aerospace fields
Hot-line:
Details
Introduction | |||
A soft irradiated cross-linked fluororubber heat-shrinkable tube is used for the connection, insulation, protection, end treatment or stress relief of various wires and cables in military equipment requiring high temperature resistance, oil resistance and chemical solvent resistance environment. Insulation protection or coating of wiring, coating of electronic components, etc. |
Features | |||
Operating temperature: -55~200 ℃ | |||
Minimum full shrinkage temperature: 175 ℃ | |||
Shrink ratio: 2:1 | |||
GJB 7273-2011 compliant | |||
Excellent high temperature resistance, solvent resistance, oil resistance, chemical corrosion resistance | |||
Soft, Flame Retardant, Wear Resistant |
Technical data | ||||
Property | Test Method | Value | ||
Longitudinal change rate | GJB 7273-2011 | -20%~20% | ||
Restricted shrinkage(200℃/30m) | GJB 7273-2011 | No cracks on the surface | ||
Water absorption (23℃/24h) | GJB 7273-2011 | ≤0.5% | ||
Tensile Strength | GJB 7273-2011 | ≥11.0MPa | ||
Breakdown elongation | GJB 7273-2011 | ≥250% | ||
Heat shock(300℃/4h) | GJB 7273-2011 | No cracks, no flow, no dripping on the surface | ||
Aging(250℃/168h) Tensile Strength Breakdown elongation |
GJB 7273-2011 | ≥11.0MPa ≥200% |
||
Dielectric strength | GJB 7273-2011 | ≥7.9kV/mm | ||
Insulation withstand voltage(AC2500V·1min.) | GJB 7273-2011 | Not broken down | ||
Volume resistivity | GJB 7273-2011 | ≥1.0×109Ω·cm | ||
Liquid resistance(23℃/24h) Tensile Strength Breakdown elongation |
GJB 7273-2011 | ≥11.0MPa ≥250% |
||
flame retardancy | GJB 7273-2011 | The continuous burning time does not exceed 60S after leaving the fire | ||
Copper corrosion(175℃/16h) | GJB 7273-2011 | No dents or blackening of the copper surface | ||
low temperature flexibility(-55℃/4h) | GJB 7273-2011 | No cracks on the surface | ||
High and low temperature impact(-55℃/250℃) | GJB 7273-2011 | Tensile Strength≥11.0MPa Breakdown elongation≥200% |
||
salt spray | GJB 150.11 | Tensile Strength≥11.0MPa Breakdown elongation≥200% |
||
damp heat | GJB 150.9 | Tensile Strength≥11.0MPa Breakdown elongation≥200% |
||
mold | GJB 150.10 | The degree of mold growth is not worse than grade 1 |
Dimension | |||||
Size | As Supplied(mm) | After shrink (mm) | Wire mass(Max.) | Standard length | |
S10 | Inner Diameter(Min.) | Inner Diameter (Max.) | Wall thickness | g/m | m |
2.4/1.2 | 2.4 | 1.2 | 0.60±0.10 | 9.8 | 100 |
3.2/1.6 | 3.2 | 1.6 | 0.76±0.13 | 11.8 | 100 |
4.8/2.4 | 4.8 | 2.4 | 0.89±0.18 | 17.5 | 100 |
6.4/3.2 | 6.4 | 3.2 | 0.89±0.18 | 20.6 | 61 |
9.5/4.8 | 9.5 | 4.8 | 0.89±0.18 | 33.7 | 61 |
12.7/6.4 | 12.7 | 6.4 | 0.89±0.18 | 60.7 | 61 |
15.9/7.9 | 15.9 | 7.9 | 1.07±0.21 | 76 | 61 |
19.1/9.5 | 19.1 | 9.5 | 1.07±0.21 | 88.8 | 61 |
22.2/11.1 | 22.2 | 11.1 | 1.25±0.30 | 140 | 61 |
25.4/12.7 | 25.4 | 12.7 | 1.25±0.30 | 151 | 61 |
38.1/19.1 | 38.1 | 19.1 | 1.40±0.38 | 252.3 | 30.5 |
50.8/25.4 | 50.8 | 25.4 | 1.65±0.43 | 300.5 | 30.5 |
Ordering instructions: please order by "model-specification-color", such as S10-9.5/4.8-0 | |||
Color: Black (-0) should be used |
Cross reference | |
Raychem/TE: RW-200/RW-200-E |
Color: Black (-0) should be used